Relia® Quality Wear Resistant Plates
Relia® is a range of high hardness, conventional low-alloyed martensitic steels, which obtain their hardness through intense water quenching during plate manufacturing. Relia® steel plates offer outstanding resistance to abrasion typically 3 to 6 times higher than 355MPa-class construction steel, although the actual performance may vary depending on the type of wear and operating conditions. The use of Relia® plates will extend the service life of wear parts and machinery components over standard construction steel, without sacrificing on quick and easy fabrication in the workshop. Relia® plates are available in 3 nominal hardness levels 400, 450 and 500 HBW and 2 product specification levels to meet a wide range of practical requirements:structural parts.
Relia® Premium is the preferred solution for consistent and reliable processing behavior in the workshop combined with optimal in service performance.
Relia® 400, 450, 500 and the Relia® Premium series are proprietary grades developed by Industeel. There exists no engineering standard for plates intended for wear resistant applications.
Typical values (weight %)
|Technical characteristics||Relia® 400||Relia® 400 Premium||Relia® 450||Relia® 450 Premium||Relia® 500||Relia® 500 Premium|
|Cr + Ni + Mo||1.5||1.6||2.0|
|Nb + V + Ti||0.10||0.12||0.12|
|Tensile test(1)||YS 0.5 (MPa)||1100||1100||1200||1200||1400||1400|
|Total Elong (%)||13||13||10||10||10||10|
|CVNImpact test(5)||Temperature (°C)||-20||-20||-20|
|Average energy (J)||27||27||27|
Notes: (1) Typical values for 15 mm plate thickness (provided for reference information only)
(2) The plate is deep hardened to min 90% of the specified range for surface hardness
(3) Up to 20 mm; otherwise max 0.56 and 0,62 for 400 and 450 – class respectively
(4) CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Cu+Ni)/15
(5) After prior agreement; thickness limitation may apply
For more technical details :