Super – austenitic
UR™ 367
STANDARDS | |||||
---|---|---|---|---|---|
INDUSTEEL TRADEMARKS | UNS | ASTM | EURONORMS EN | SUS | |
UR™ 367 | N08367 | - | - |
- | |
CHEMICAL ANALYSIS (%WEIGHT) | |||||
C | Cr | Ni | Mo | N | Others |
< 0,030 | 20 | 24,5 | 6 | 0,23 | - |
PROPERTIES | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
0,2 Y.S. - Rp 0,2min ASTM / EN | 0,2 Y.S. - Rp 0,2(2) typical value | UTS - Rm min ASTM / EN | UTS - Rm(2) typical value | EI-A(1)% | PREN(4) | HOMOLOGATIONS | ||||
MPa | Ksi | MPa | Ksi | MPa | Ksi | MPa | Ksi | Last revised | ||
310 | 45 | 365 | 53 | 655 | 95 | 710 | 103 | 35 | 43 |
APPLICATIONS | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
CHEMICAL INDUSTRIES | PROCESS INDUSTRIES | WATER TREATMENT | STORAGE & TRANSPORTATION | ||||||||
Nitric Acid | Sulfuric Acid | Polymer & other acids | Fertilisers | Pulp & Paper | Hydrome-tallurgy | Sea water & desalination | Fresh water & Tanks | Waste Water | Chemical Tanks | Cryogenic Tanks | Renewable |
POWER GENERATION | OIL & GAS | CONSTRUCTION | ||||||
---|---|---|---|---|---|---|---|---|
Nuclear | Pollution control | Hydroelectric | Renewable | Off & Onshore & production | Refining & Gas processing | Petrochemical | Architecture | Bridges |
For more technical details :
UR™ 367
Download the complete datasheet
(1) Indicative typical values
(2) Indicative typical values for thickness 20 mm at RT for transverse direction
(3) Hardening 496°C (925°F), 4h, air cooling
(4) PREN = Cr + 3.3 Mo + 16N
(5) PRENW = Cr + 3.3(Mo + 0.5W) + 16N
(6) HT: mechanical properties depend on heat treatment